MECHANISM OF CROSS BREAKS DEFECT FORMATION AND COUNTERMEASURES Thus, resulting harmfulness from the cross breaks may be diminished or eliminated by controlling profile and optimization of uncoilling operation.

横折缺陷的产生机理与治理对策在此基础上，提出了生产中控制板形和优化开卷操作以消除和减轻横折危害的措施。

It is necessary to establish rational elongation and tension, control the quality of coming strip strictly, to avoid cross breaks, improve the surface quality of strip.

制定合理的伸长率和张力制度，严格来料质量要求，可以避免横折印缺陷的产生，提高平整带钢的表面质量。

Cause Analysis of Cross Breaks of Chromium-Free Fingerprint Resistant Sheet and Corresponding Countermeasures

无铬耐指纹板表面皱纹缺陷产生原因分析及对策

Cross breaks are formed on the surface of cold rolled and tempered strip during temper rolling, which influence the surface quality and mechanical characteristics of the temper rolled strip.

冷轧退火后的带钢在平整过程中产生横折印缺陷，严重影响平整后带钢的表面质量及其力学性能。